Two-components, excellent compromise between curing behavior and open time
![](https://www.aerox.es/wp-content/uploads/2021/05/CertificacionDNV-1024x315.png)
Products
Polymer Solutions for Wind Turbine Rotor Blades
We strive to offer our customers a complete portfolio of products, so all blade finish layers are provided from one single source. Our product mix includes gel coats, filler & putties, topcoats & primers and LEP, with versions for both manufacture and repair of blades. With regard structural products, our portfolio includes bonding paste solutions both in glass filled and toughened technologies to better support all our customer needs.
Our deep material knowhow in both Epoxy and PU chemistry technologies, together with our blade manufacturing expertise in the field, makes us the best partner for your future product developments.Our goal is to get you outstanding materials, in line with the most demanding physical properties performance and in extreme weather conditions. We target to reduce your production takt time while balancing material cost and the overall blade weight.
Filter by:
Manufacturing Process
Aplication
Technology
Glass Filled
Two-components, excellent compromise between curing behavior and open time
old name
Mix Ratio | 100:45 |
Ultimate Tg | >90 |
Sag resistance | >20 mm |
Open time | |
Processability |
Thoughened
Two-components, High fracture toughness response, low density
old name
Mix Ratio | 100:33 |
Ultimate Tg | >75 |
Sag resistance | >20 mm |
Open time | |
Processability |
Repairs
old name
Epoxy Based
Two-components, Epoxy based, easy to sand, fast curing, smoth surface.
old name
Mix Ratio | 100:56 |
Gel time | >35 |
Sag resistance | >4 |
Fatigue response | |
Drying | |
Easy to sand |
Polyurethane Based
Two-components, Poliurethane based, easy to sand and very fast curing time.
Two versions (SLOW and FAST) are available, designed as a pore filler and can be pigmented in different colors (RAL).
Available version for service (repair and maintenance).
old name
Mix Ratio | 100:33 |
Gel time | >5 m |
Sag Resistance | >4 |
Drying | |
Easy to sand |
old name
LOW UV RESISTANCE
Two-components, traslucent, easy sanding, fast curing, suitable for infusion prepreg/process
old name
Mix Ratio | 100:20 |
Ultimate Tg | >90 |
Gel Time | >12 |
Easy to sand | |
Drying |
LOW UV RESISTANCE
Two-components, traslucent, easy sanding, fast curing, suitable for infusion prepreg/process
old name
Mix Ratio | 100:20 |
Ultimate Tg | >90 |
Gel Time | >12 |
Easy to sand | |
Drying |
HIGH UV RESISTANCE
Two-components, high UV resistance, coloured, easy sanding, suitable for infusion/prepreg process
old name
Mix Ratio | 100:19 |
Ultimate Tg | >90 |
Gel Time | >12 min |
Easy to sand | |
Drying |
HIGH UV RESISTANCE
Two-components, high UV resistance, traslucent, easy sanding, fast curing, suitable for prepreg/infusion process
old name
Mix Ratio | 100:20 |
Ultimate Tg | >90 |
Gel Time | >12 |
Easy to sand | |
Drying |
Fast Curing / Matt
Two-components, fast curing, solvent-based paint, very good surface finish.
old name
Mix Ratio | 100:18 |
Gel time | >4 |
Sag Resistance | >200 |
VOC'S content | |
Color Retention |
Polyurethane Based
Two-components, Poliurethane based, fast curing time, proven efficiency, high UV, rain and abrasion resistance
old name
Mix Ratio | 100:50 |
PULL-OFF ADHESION | >6 Mpa |
Rain Erosion Resistance | >16hrs(Small spots of erosion) |
Gel time | >14 min |
Easy to use |